點(diǎn)擊圖片查看原圖| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.05 | 23/23℃ | |
| 燃燒性 | File NO.E196075 | 1/16"HB | |||
| 熔融指數(shù) | 200℃ 10kg | ISO1133 | 22 | g/10min | |
| 200℃ 5kg | ASTM D-1238 | 1.8 | g/10min | ||
| 機(jī)械性能 | 引張強(qiáng)度 | ASTM D-638 | 480 | kg/cm2 | |
| IZOD沖擊強(qiáng)度 | 1/8" | ASTM D-256 | 20 | kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 116 | R | ||
| 伸長(zhǎng)率 | ASTM D-790 | 20 | % | ||
| 彎曲彈性率 | ASTM D-790 | 2.7 | 104kg/cm2 | ||
| 彎曲強(qiáng)度 | ASTM D-790 | 790 | kg/cm2 | ||
| IZOD沖擊強(qiáng)度 | 1/4〃 | ASTM D-256 | 18 | kg.cm/cm | |
| 熱性能 | 維卡軟化點(diǎn) | ASTM D-1525 | 105(221) | ℃(℉) | |
| 熱變形溫度 | 退火 | ASTM D-648 | 99(210) | ℃(℉) | |
| 未退火 | ASTM D-648 | 88(190) | ℃(℉) | ||